ZJ-940
Silane modified adhesive for industrial electronics

ZJ-940 is a single component silane modified polyether adhesive that reacts with moisture in the air during use. After curing, it has good adhesion to various substrates, including metal, plastic, and glass.

Product features

Environmentally friendly products, solvent free, environmentally friendly;

Excellent adhesion performance for various substrates with different polarity;

Good extrudability and wide temperature adaptation range;

Faster surface drying time and higher initial strength.

Product parameters
The following data is for reference only

Product Name

ZJ-940

Product type

Silane modified polyether resin

Curing method

Moisture cure

Appearance

White, black

Viscosity(23℃,10rpm,cps)

10000±1000

Density(g/cm3)

1.35

Surface drying time(min)

10

24h curing depth(mm)

2.0

Complete curing time(d)

7

Hardness(Shore A)

61

Tensile strength(MPa)

3.65

Elongation at break(%)

152

Adhesive strength (glass to aluminum, MPa)

2.35

Applicable temperature range(℃)

-40~120

High temperature resistance 150 ℃ baking for 2 days without affecting adhesion

Thermal conductivity (W/mk)

0.3

Surface resistance(Ω)

6.3*1013

Shelf life (months)

12

Color and packaging

ZJ-940 silane modified adhesive provides 330mL hard tube

Storage and expiration date

When the ZJ-940 silane modified adhesive is stored in its original packaging in a cool, dry, and ventilated place, the product has a shelf life of 12 months from the date of production.